摘要 |
Magnetic materials having a coercivity not less than about 1000 Oersted are prepared in a single step procedure. A molten mixture of a desired composition having a relatively high boron content is cooled at a rate slower than about 105 degrees Celsius per second. Preferably, the molten mixture is cooled by depositing it on a chilled surface such that it forms a layer between about 120 and about 300, and preferably between about 120 and about 150, microns thick.
|