A process for the extrusion of polyethylene having a broad molecular weight distribution wherein the polyethylene is prepared in pellet form, said extrusion taking place in a pelletizing extruder having one or more zones essentially filled with polyethylene and two or more zones partially filled with polyethylene including a feed zone comprising (i) introducing the polyethylene into the extruder at a temperature sufficient to melt the polyethylene; (ii) introducing a mixture of an inert gas and oxygen into at least one partially filled zone with the exception of the feed zone, said mixture containing about 1 to about 21 percent by volume oxygen based on the volume of the gaseous mixture; (iii) passing the molten polyethylene through each zone at melt temperature; and (iv) extruding the polyethylene into pellets and cooling same. |