A nodular or compacted graphite iron contains up to 6% aluminum, with high strength and good ductility over a wide temperature range, combined with excellent hot oxidation resistance and improved thermal fatigue resistance compared to ductile and SiMo ductile irons. The iron alloy of the invention contains, in addition to iron, from about 1 to about 6% aluminum, from about 2 to about 4.5% silicon, carbon in an amount where the weight percent carbon plus 1/3 the weight percent of silicon is up to about 5.2%, greater than or equal to about 0.02% cerium and up to about 1.5% molybdenum. All percentages are based on the total weight of the composition. The compositions may further contain up to about 7% nickel by weight.
|