Method of producing Ni-Cu-Zn ferrite material

摘要

A method of producing a Ni-Cu-Zn ferrite material comprises the steps of preparing a mixture of an iron compound powder having a specific surface area of about 8.5 m2/g or more, a nickel compound powder, copper compound powder and a zinc compound powder, the mixture having a specific surface area of about 8.0 m2/g or more; pre-calcining the mixture such that the pre-calcined mixture has a surface area of about 5.0 m2/g or more and a spinel crystal synthesizability within a range of about 80.5% to 98%; and milling the pre-calcined mixture to obtain a powder of a Ni-Cu-Zn ferrite material having a specific surface area of about 6.0 m2/g or more.