| 摘要 |
A metallic press die having an edge portion or high pressure portion for processing a workpiece therewith is made by overlaying a welding material to that portion of a base material for the metallic press die which forms the edge portion or high pressure portion, and then machining an overlaid portion into a predetermined shape of the edge portion or high pressure portion. The welding material has a hardness after welding of HRC 45 or below. After the machining step, the overlaid portion is subjected to a subzero treatment to increase the hardness of the overlaid portion. The welding material contains, as a basic composition thereof, 0.5-1.5% by weight of carbon (C), 0.2 -2.0% by weight of silicon (Si), 0.3-6.0% by weight of manganese (Mn), 0.3-10.0% by weight of chromium (Cr), 0.3-10.0% by weight of cobalt (Co), and the remaining parts of iron (Fe) inclusive of unavoidable impurities, and wherein a starting temperature of martensitic transformation is 150 DEG C. or below.
|