A glass flux composition consisting essentially in mol percent of 3.0-13.0 lithium oxide, 0.5-3.5 potassium oxide, 2.5-7.0 sodium oxide, 0.5-2.5 zinc oxide, 2.0-8.0 aluminium oxide, 15-30 boron oxide, 44-68 silica, 1.0-7.0 zirconium oxide, 0-4.0 calcium oxide, 0-3.0 lanthanum oxide, 0-1.0 other rare earth metal oxide, 0-1.0 yttrium oxide, 0-4.0 magnesium oxide,0-4.0 strontium oxide, 0-4.0 titanium oxide, 0-10 phosphorus pentoxide, 0-1.5 lead oxide and 0-13.0 fluoride is useful for preparing an enamel or cover flux composition, especially for application to ceramic ware.
|