发明名称 |
Magnetic disk substrate and method of manufacturing the same. |
摘要 |
<p>A magnetic disk substrate comprising 0.5 wt% to 1.0 wt% of Mo, 0.03 wt% to 0.5 wt% of O + 2N + 0.75C, and a balance of Ti. The alloy plate having a composition of above range is cold-rolled at a rolling ratio of 30% or more to form a magnetic disk substrate material, and the material is thermal-flattened under the following condition: 500 </= T </= -(150/11).t + 7850/11 1 </= t where T represents a thermal-flattening temperature ( DEG C), and t represents a thermal-flattening time (houre), thereby obtaining a magnetic disk substrate having the average grain size of 30 mu m or less.</p> |
申请公布号 |
EP0402913(A2) |
申请公布日期 |
1990.12.19 |
申请号 |
EP19900111229 |
申请日期 |
1990.06.13 |
申请人 |
NKK CORPORATION |
发明人 |
FUKAI, HIDEAKI, C/O PATENT & LICENSE DEPT.;SUENAGA, HIROYOSHI, C/O PATENT & LICENSE DEPT.;MINAKAWA, KUNINORI, C/O PATENT & LICENSE DEPT. |
分类号 |
G11B5/73;G11B5/84 |
主分类号 |
G11B5/73 |
代理机构 |
|
代理人 |
|
主权项 |
|
地址 |
|