Porous silica microspheres having silanol-enriched and silanized surfaces.

摘要

A chromatographic material having improved crush resistance and a high level of surface silanol groups comprises porous silica microspheres having an average diameter of about 0.5 to about 35 mu m, substantially all of said microspheres having a diameter ranging from about 0.5 to about 1.5 times said average diameter; said microspheres comprising a plurality of substantially uniform-size colloidal particles, having a silica surface, arranged in an interconnected three-dimensional lattice; said colloidal particles occupying less than about 50 volume percent of said microspheres with the remaining volume being occupied by interconnected pores having substantially uniform pore size distribution; said microspheres having a total concentration of silanol groups from about 6 to about 16 mu mol/m<2>. The material may be reacted with a silanizing agent to generate a completely silanized surface.