| 摘要 |
PURPOSE:To obtain the titled resin compound having excellent heat-resistance and corrosion-resistance and suitable as paint and lining, by compounding an unsaturated polyester resin with a flaky inorganic material subjected to a specific treatment. CONSTITUTION:(A) 100pts.(wt.) of a flaky inorganic material having a diameter of <=3mmphi and a thickness of 1-10mu (e.g. glass flakes, mica, etc.) is immersed in (B) a solution obtained by dissolving or dispersing 0.5-5pts. of a silane coupling agent (e.g. vinyl triethoxysilane) in a polymerizable monomer (e.g. styrene), at <=130 deg.C. The obtained wet inorganic material is added to a resin liquid composed of an unsaturated polyester and a polymerizable monomer (preferably same as the above monomer) in an amount of 10-40wt%.
|