| 摘要 |
<P>L'INVENTION CONCERNE DES ALLIAGES A BASE D'AL PRESENTANT UNE GRANDE STABILITE A CHAUD.</P><P>CES ALLIAGES CONTIENNENT DE 5 A 20 (EN POIDS) EN FE, PLUS DE 0,05 NI, PLUS DE 0,5 MO AVEC NIMO8 ET MONI0,5, RESTE AL AVEC DES ADDITIONS EVENTUELLES ALLANT JUSQU'A 5 EN POIDS D'UN (OU PLUSIEURS DES) ELEMENT(S) SUIVANT(S): SI, MN, CR, TI, HF, ZR, V, W, NB.</P><P>CES ALLIAGES SONT OBTENUS PAR SOLIDIFICATION RAPIDE (10CSECONDE) ET POSSEDENT UNE STABILITE A CHAUD ELEVEE JUSQUE VERS 450-500C.</P>
|