<p>HIGH STRENGTH FERRITIC ALLOY A high-strength ferritic alloy useful for fast reactor duct and cladding applications wherein an iron base contains from about 9% to about 13% by weight chromium, from about 4.% to about 8% by weight molybdenum, from about 0.2% to about 0.8% by weight niobium, from about 0.1% to about 0.3% by weight vanadium, from about 0.2% to about 0.8%, by weight silicon, from about 0.2% to about 0.8% by weight manganese, a maximum of about 0.05% by weight nitrogen, a maximum of about 0.02% by weight sulfur, a maximum of about 0.02% by weight phosphorous, and from about 0.04% to about 0.12% by weight carbon.</p> |