| 摘要 |
本发明公开了白光发光二极管用荧光粉及制备方法，白光发光二极管用荧光粉化学结构式为：Y<SUB>3－x</SUB>Ba<SUB>x</SUB>Al<SUB>5</SUB>O<SUB>12</SUB>:Ce，其中x为0.3～1.8。制备步骤：(1)称取Y<SUB>2</SUB>O<SUB>3</SUB>、BaCO<SUB>3</SUB>、Al<SUB>2</SUB>O<SUB>3</SUB>、CeO<SUB>2</SUB>、BaF<SUB>2</SUB>和H<SUB>3</SUB>BO<SUB>3</SUB>；(2)将BaF<SUB>2</SUB>和H<SUB>3</SUB>BO<SUB>3</SUB>放入玛瑙研钵中研混均匀，再加入Y<SUB>2</SUB>O<SUB>3</SUB>、BaCO<SUB>3</SUB>、Al<SUB>2</SUB>O<SUB>3</SUB>和CeO<SUB>2</SUB>，研磨混匀得混合物；(3)放入刚玉坩埚中，在含氢气的氮气流中于1050～1300℃下灼烧2～4h，得白光发光二极管用荧光粉。通过本发明方法生产的白光发光二极管用荧光粉，发光强度比Y<SUB>3</SUB>Al<SUB>5</SUB>O<SUB>12</SUB>:Ce的发光强度至少大10％以上，用于照明、汽车、个人通讯设备等领域。 |