Iron-Based Alloys and Methods of Making and Use Thereof |
摘要 |
An iron-based alloy includes (in weight percent) carbon from about 1 to about 2 percent; manganese up to about 1 percent; silicon up to about 1 percent; nickel up to about 4 percent; chromium from about 10 to about 25 percent; molybdenum from about 5 to about 20 percent; tungsten up to about 4 percent; cobalt from about 17 to about 23 percent; vanadium up to about 1.5 percent; boron up to about 0.2 percent; sulfur up to about 0.03 percent; nitrogen up to about 0.4 percent; phosphorus up to about 0.06 percent; niobium up to about 4 percent; iron from about 35 to about 55 percent; and incidental impurities. The chromium/molybdenum ratio of the iron-based alloy is from about 1 to about 2.5. The alloy is suitable for use in elevated temperature applications, such as valve seat inserts for combustion engines. |
申请公布号 |
US2016245132(A1) |
申请公布日期 |
2016.08.25 |
申请号 |
US201615147087 |
申请日期 |
2016.05.05 |
申请人 |
L.E. Jones Company |
发明人 |
Qiao Cong Yue;Doll David;Trudeau Todd;Vennema Peter |
分类号 |
F01L3/02;C22C38/52;C22C38/48;C22C38/46;C21D6/02;C22C38/04;C22C38/02;C22C38/00;C21D9/00;C21D1/18;C22C38/54;C22C38/44 |
主分类号 |
F01L3/02 |
代理机构 |
|
代理人 |
|
主权项 |
1. An iron-based alloy comprising, in weight percent:
carbon from about 1 to about 2 percent; manganese up to about 1 percent; silicon up to about 1 percent; nickel up to about 4 percent; chromium from about 10 to about 25 percent; molybdenum from about 5 to about 20 percent; tungsten up to about 4 percent; cobalt from about 17 to about 23 percent; vanadium up to about 1.5 percent; boron up to about 0.2 percent; sulfur up to about 0.03 percent; nitrogen from about 0.1 to about 0.4 percent; phosphorus up to about 0.06 percent; niobium up to about 4 percent; iron from about 35 to about 55 percent; and incidental impurities; wherein the chromium/molybdenum ratio of the iron-based alloy is from about 1 to about 2.5. |