PROCESS FOR THE PREPARATION OF A COMPOSITION COMPRISING HETEROPHASIC PROPYLENE CO-POLYMER AND TALC |
摘要 |
The invention relates to a process for the preparation of a composition comprising a heterophasic propylene copolymer, a propylene copolymer and talc, wherein the heterophasic propylene copolymer consists of (a) a propylene-based matrix, wherein the propylene-based matrix consists of a propylene homopolymer and/or a propylene-α-olefin copolymer consisting of at least 70% by mass of propylene and up to 30% by mass of α-olefin based on the total mass of the propylene-based matrix, wherein the propylene-based matrix is present in an amount of 60 to 95 wt % based on the total heterophasic propylene copolymer and (b) a dispersed ethylene-α-olefin copolymer, wherein the dispersed ethylene-α-olefin copolymer is present in an amount of 40 to 5 wt % based on the total heterophasic propylene copolymer and wherein the sum of the total amount of propylene-based matrix and total amount of the dispersed ethylene-α-olefin copolymer in the heterophasic propylene copolymer is 00 wt %, wherein the composition has a desired melt flow index in the range of 1 to 200 dg/min as measured according to ISO1133 (2.16 kg/230° C.) comprising the steps of (a) melt-mixing a propylene copolymer with a talc to obtain a masterbatch (b) melt-mixing the masterbatch with 1 the heterophasic propylene copolymer and a peroxide to obtain the composition comprising a heterophasic propylene copolymer, a propylene copolymer and talc, wherein the amount of peroxide is chosen such that a composition comprising a heterophasic propylene copolymer, a propylene copolymer and talc having the desired melt flow index is obtained. |
申请公布号 |
US2015232652(A1) |
申请公布日期 |
2015.08.20 |
申请号 |
US201314429217 |
申请日期 |
2013.09.17 |
申请人 |
HERKLOTS Marc;SAUDI BASIC INDUSTRIES CORPORATION |
发明人 |
Herklots Marc |
分类号 |
C08L23/14;C08L23/12;C08L23/08 |
主分类号 |
C08L23/14 |
代理机构 |
|
代理人 |
|
主权项 |
1. A process for the preparation of a composition comprising a heterophasic propylene copolymer and talc,
wherein the heterophasic propylene copolymer consists of (a) a propylene-based matrix, wherein the propylene-based matrix consists of a propylene homopolymer and/or a propylene-α-olefin copolymer consisting of at least 70% by mass of propylene and up to 30% by mass of ethylene, based on the total mass of the propylene-based matrix wherein the propylene-based matrix is present in an amount of 60 to 95 wt % based on the total heterophasic propylene copolymer, and (b) a dispersed ethylene-α-olefin copolymer, wherein the dispersed ethylene-α-olefin copolymer is present in an amount of 40 to 5 wt % based on the total heterophasic propylene copolymer and wherein the sum of the total amount of propylene-based matrix and total amount of the dispersed ethylene-α-olefin copolymer in the heterophasic propylene copolymer is 100 wt %, wherein the composition has a desired melt flow index in the range of 1 to 200 dg/min as measured according to ISO1133 (2.16 kg/230° C.),wherein at least part of the talc is surface-modified and wherein the amount of talc in the composition is from about 0.5 to at most 5 wt % based on the heterophasic propylene copolymer,
comprising the step of
(a) melt-mixing the heterophasic propylene copolymer with the talc and a peroxide,wherein the amount of peroxide is chosen such that a composition comprising a heterophasic propylene copolymer and talc having the desired melt flow index is obtained, wherein the α-olefin in the propylene-α-olefin copolymer is selected from the group of α-olefins having 2 or 4-10 carbon atoms, wherein the amount of ethylene in the ethylene-α-olefin copolymer is in the range of 20-65 wt % based on the ethylene-α-olefin copolymer, and wherein the α-olefin in the ethylene-α-olefin copolymer is chosen from the group of α-olefins having 3 to 8 carbon atoms and any mixtures thereof. |