发明名称 |
α alumina sintered body for production of sapphire single crystal |
摘要 |
A method for producing an α alumina sintered body for the production of a sapphire single crystal characterized in that a relative density is 60% or more, a closed porosity is 10% or less, a purity is 99.99% by mass or more, each content of Si, Na, Ca, Fe, Cu and Mg is 10 ppm or less, and a volume is 1 cm3 or more, and the α alumina sintered body can be obtained by mixing 100 parts by weight of an α alumina with 1 part by weight or more and 20 parts by weight or less of an α alumina precursor to obtain a mixture, forming a compact from the obtained mixture, and firing the obtained compact. |
申请公布号 |
US8859446(B2) |
申请公布日期 |
2014.10.14 |
申请号 |
US201113341154 |
申请日期 |
2011.12.30 |
申请人 |
Sumitomo Chemical Company, Limited |
发明人 |
Ozaki Hirotaka;Fujiwara Shinji |
分类号 |
C04B35/00;C04B35/111;C30B1/12;C30B29/20;C04B35/64;C01F7/02 |
主分类号 |
C04B35/00 |
代理机构 |
Sughrue Mion, PLLC |
代理人 |
Sughrue Mion, PLLC |
主权项 |
1. A method for producing an α alumina sintered body for the production of a sapphire single crystal, comprising the steps of:
Step (a): mixing 100 parts by weight of an α alumina with 1 part by weight or more and 10 parts by weight or less of an α alumina precursor to obtain a mixture in a powder form or a granule form; Step (b): forming a compact from the mixture; and Step (c): firing the compact to obtain an α alumina sintered body. |