发明名称 |
Cubic boron nitride sintered body tool |
摘要 |
The cubic boron nitride sintered body tool of the present invention has a cubic boron nitride sintered body including cubic boron nitride particles and a binder phase at at least a cutting edge. The cubic boron nitride sintered body includes 40-70 volume % of cubic boron nitride particles. The binder phase includes a first component and a second component. The first component includes TiC, and the second component includes one or both of TiB2 and AlB2. When the X-ray diffraction intensity of plane (200) of the first component is I1 and the X-ray diffraction intensity of plane (101) of said second component is I2, I1 is the maximum of the X-ray diffraction intensity of all components in the cubic boron nitride sintered body excluding the cubic boron nitride particles, and satisfies 0.01≦I2/I1≦0.1. |
申请公布号 |
US8822361(B2) |
申请公布日期 |
2014.09.02 |
申请号 |
US201113521325 |
申请日期 |
2011.10.07 |
申请人 |
Sumitomo Electric Hardmetal Corp. |
发明人 |
Okamura Katsumi;Abe Machiko;Kukino Satoru |
分类号 |
C04B35/5831;C04B35/628;B22F1/02;C22C26/00;B22F5/00 |
主分类号 |
C04B35/5831 |
代理机构 |
Venable LLP |
代理人 |
Venable LLP ;Sartori Michael A.;Aga Tamatane J. |
主权项 |
1. A cubic boron nitride sintered body tool having a cubic boron nitride sintered body including cubic boron nitride particles and a binder phase at at least a cutting edge, wherein
said cubic boron nitride sintered body includes 40-70 volume % of said cubic boron nitride particles, said binder phase includes a first component and a second component, said first component is TiC, said second component is one or both of TiB2 and AlB2, and when X-ray diffraction intensity of plane (200) of said first component is I1 and X-ray diffraction intensity of plane (101) of said second component is I2, said I1 is the maximum of the X-ray diffraction intensity of all components in said cubic boron nitride sintered body excluding said cubic boron nitride particles, and satisfies 0.01≦I2/I1≦0.1, wherein at least a portion of said second component is present so as to come into contact with a surface of the cubic boron nitride particle, a surface-constituting ratio of said second component at the surface of the cubic boron nitride particle is 20-70%, and said binder phase includes 1-10 volume % of said second component. |