| 摘要 |
An antireflection film, comprising a film including: hollow particles; and a binder bonding the particles, wherein: the binder contains voids; and the binder contains 10 or less voids each having a cross-sectional area of 1,000 nm2 or more with respect to 1 mum2 of a cross-sectional area of the binder. A method of producing the film, comprising: forming a paint into a film by applying the paint onto a substrate, the paint containing hollow particles, a binder, and a solvent, in which a content of the particles is 50-85 wt % and a content of the binder is 15-40 wt % with respect to a total weight of a solid content of the paint, and the paint has a viscosity of 1.3-2 mPa·s at its film-forming temperature; and drying the film. |