High-strength hot rolled steel sheet being free from peeling and excellent in surface properties and burring properties, and method for manufacturing the same

摘要

This hot rolled steel contains, in terms of mass %, C: 0.01 to 0.1%, Si: 0.01 to 0.1%, Mn: 0.1 to 3%, P: not more than 0.1%, S: not more than 0.03%, Al: 0.001 to 1%, N: not more than 0.01%, Nb: 0.005 to 0.08%, and Ti: 0.001 to 0.2%, with a remainder being iron and unavoidable impurities, wherein a formula: [Nb]×[C]≦̸4.34×10−3 is satisfied, a grain boundary density of solid solution C is not less than 1 atom/nm2 and not more than 4.5 atoms/nm2, and a grain size of cementite grains precipitated at grain boundaries within the steel sheet is not more than 1 μm.