| 摘要 |
<p>Provided is a laminated body capable of reducing the surface roughness of the surface of a roughening-treated cured body layer, and increasing the adhesive strength between the cured body layer and a metal layer. A laminated body includes a cured body layer formed by: laminating a resin film on a substrate, forming a preliminary-cured body layer by preliminary-curing the resin film at 100° C. to 200° C., and performing a roughening treatment on the surface of the cured object layer at 55° C. to 80° C. The resin film is formed from a resin composition including an epoxy resin, a phenol curing agent, a curing accelerator, and a surface-treated substance which is a surface treated, using 0.5 to 3.5 parts by weight of a silane coupling agent, on 100 parts by weight of inorganic filler with a mean particle diameter of 0.05 to 1.5μm. The silane coupling agent has an epoxy group, an imidazole group, or an amino group.</p> |