The throw-away tip has a shape of substantially flat plate, comprising from 1 to 30% by weight of binder phase comprising at least one kind of Co and Ni, and 70 to 99% by weight of carbonitride phase comprising composite metal carbonitride of Ti and one or more kind other than Ti among metals of groups 4a, 5a and 6a of the Periodic Table, wherein the mean grain size of the carbonitride phase is 1.5 mum or less, while flexural strength test pieces which are cut out of ten throw-away tips including the side face thereof show flexural strength with a Weibull coefficient of 5 or higher. Throw-away tips having fine carbonitride phase structure and high cutting performance can be made with less variance among individual throw-away tips. |