Disclosed is a molded or extruded thermoplastic article including a polyamide composition including (a) a polyamide resin (b) 0.1 to 10 weight percent of one or more polyhydric alcohols (c) 0 to 3 weight percent of a co-stabilizer selected from the group consisting of secondary aryl amines, hindered amine light stabilizers, and mixtures thereof; (d) 0 to less than 10 weight percent of one or more reinforcement agents; and (e) 0 to 50 weight percent polymeric toughener including a reactive functional group and/or a metal salt of a carboxylic acid; and wherein 4 mm test bars prepared from the polyamide composition, and exposed at an test temperature of 150° C. for a test period of about 1000 hours, have, on average, a retention of strain at break of greater than 80 percent compared with a control exposed at the said test temperature for 72 hours.
|