| 摘要 |
FIELD: polymer materials. ^ SUBSTANCE: invention relates to polyurethane elastomers suited to manufacture polyurethane articles. Composition according to invention contains (i) 70.6-74.8% polyfurite urethane prepolymer prepared by reaction between 2.1 mile 2,4-tolylenediisocyanate and 1.0 mole poly(oxytetramethylene glycol) with molecular weight 1500 and (ii) liquid curing agent (to 100%), which is a mixture of 3,3'-dichloro-4,4'-diaminodiphenylmethane and poly(oxytetramethylene glycol) with molecular weight 1000 at their molar ratio 1:1. Thus obtained polyurethane elastomers show Shore hardness al a level of 93 relative units, breaking point (23°C) at a level of 38 MPa, elongation on fracture 712%, and abrasion resistance 27 mcm (according to Russian standard GOST 11529-86). Articles manufactured from these elastomers may find use for in-tube flaw inspection of oil and gas mains as well as oil storage tanks. ^ EFFECT: enlarged assortment of industrially useful elastomers. ^ 4 tbl, 6 ex |