摘要 |
<p>This invention concerns a process for coating a substrate, and an extrusion coating structure. According to the present process, the coating is provided by producing a bimodal polyethylene composition by subjecting ethylene, optionally with hydrogen and/or comonomers to polymerization or copolymerization reactions in a multistage polymerization sequence of successive polymerization stages. The polymerization reactions are carried out in the presence of a single site catalyst capable of forming a composition which comprises a low molecular weight component with an MFR<SUB>2 </SUB>of 20 g/10 min or more and a density higher than the density of the composition, and a high molecular weight component, said composition having a melt flow rate MFR<SUB>2 </SUB>of 5 g/10 min or more and a density of 915-960 kg/m<SUP>3</SUP>. The composition is extruded on the substrate as such or by adding 10 wt-% or less, calculated from the total weight of the coating, of high pressure PE-LD by blending into the extrusion composition or by coextrusion.</p> |