Aqueous polymer dispersions based on acrylic polymers in which the diameter of the individual particles is between 50 nm and 1 000 nm, and the particle distribution by weight relative to the total dry weight is as follows: a) from 50 nm to 180 nm : from 10% to 70%, preferably from 20% to 60%; b) from > 180 nm to 1 000 nm : from 30% to 90%, preferably from 40% to 80%; the said dispersions having a minimum film-forming temperature of between about 1 DEG C and 80 DEG C, which, after drying, produce films which, when subjected to heating under a nitrogen atmosphere, show a weight loss, for films about 1 mm in thickness, and for the following heating cycle, which simulates the process for preparing CRTs, from 25 DEG C to 375 DEG C from 40% to 70% by weight, from 375 DEG C to 440 DEG C for greater than 99% by weight, after the isothermal stage at 440 DEG C, the remaining residual ash being less than about 0.1% by weight.
|
申请人 |
ATOFINA;SAIJA, LEO, MARIO;LUGLI, MARIO;BECCHI, DANIELE |
发明人 |
SAIJA, LEO, MARIO;LUGLI, MARIO;BECCHI, DANIELE |