| 摘要 |
PROBLEM TO BE SOLVED: To provide olefinic thermoplastic elastomers excellent in the balance of flexibility and tensile elongation at break and low temperature impact resistance, and a method for preparing the same. SOLUTION: Olefinic thermoplastic elastomers comprise a composition which is composed of (A) more than 50 wt.% to not more than 60 wt.%, based on the entire composition, propylene homopolymer or copolymer component of propylene and other 2-8Cα-olefins which has an isotacticity of not less than 85% and (B) not less than 40 wt.% to less than 50 wt.%, based on the entire composition, copolymer component having, as the essential components, propylene and ethylene and composed of propylene and other 2-8Cα-olefins with a xylene insolubles content at room temperature of from not less than 5 wt.% to less than 10 wt.%, based on the entire composition, and a xylene soluble matter content at room temperature of from more than 30 wt.% to not more than 45 wt.%, based on the entire composition, and is prepared by the polymerization of component (B) after the polymerization of component (A).
|