| 摘要 |
The invention provides a valve seat having a suitable degree of wear resistance, which can be produced without recourse to expensive elements represented by cobalt and at a cost lower than ever before. This valve seat is formed of a wear-resistant sintered alloy having a general composition consisting essentially of, in weight ratio, 0.736 to 9.65% of nickel, 0.736 to 2.895% of copper, 0.294 to 0.965% of molybdenum, 0.12 to 6.25% of chromium, and 0.508 to 2.0% of carbon with the balance being iron, and inevitable impurities, and having a metallic structure in which there are dispersed (1) a martensite, (2) a bainite having a nucleus of sorbite and/or upper bainite and surrounding said nucleus, (3) an austenite having a high nickel concentration, and (4) a hard phase surrounding with a ferrite having a high chromium concentration and composed mainly of a chromium carbide. |