摘要 |
<p>Rolled articles such as hot rolled or cold rolled and annealed sheet and/or strip include effective amounts of vanadium in low carbon steels to produce an improved bake hardenable product especially adapted for automotive use. The use of vanadium in the alloy steel chemistry controls bake hardenability, permits solution annealing at lower temperatures in its manufacturing sequence and specifies a composition range which is more easily cast within desired limits and causes less variation in final mechanical properties. The steel has a composition consisting in weight percent of between 0.0005 and 0.1 percent carbon, between zero and less than 0.04 percent nitrogen, between zero and less than 0.5 percent of a nitride forming element, between zero and 0.5 percent aluminium, between zero and up to 2.5 percent manganese, between 0.005 and 0.6 percent vanadium with the balance iron and inevitable impurities.</p> |