| 摘要 |
Nuclear fuel rod tubes of zirconium alloy are heat treated in an induction furnace to produce a protective oxide coating two to fifteen microns in thickness. The furnace is only slightly larger than the tubes and receives the endmost eight inches of the tube. The furnace is controllable in zones along the tube. To calibrate the furnace to produce the desired temperature profile, typically a flat profile at a temperature between 650 DEG and 750 DEG C.+/-1.5 DEG C., a temperature calibration probe is provided with spaced thermocouples for sensing the temperature developed in the probe at each of the zones when heated. The probe is made of inconel 600 stainless or the like, and is dimensioned and shaped to correspond closely to the dimensions of the fuel rod tubes, including having a closed chamfered end. At the opposite end the probe protrudes from the furnace, where the thermocouple leads are terminated. The leads pass through a potting compound in the probe, such as magnesium oxide. Whereas the probe conductive structures are substantially identical to the tube, the probe responds to the electromagnetic field in the induction furnace substantially the same as does the end of the tube, permitting calibration of the induction furnace zones for a desired temperature profile, e.g., flat along the length of the tube, notwithstanding differences in induced currents that would otherwise occur due to the end of the tube or the adjacent tube material.
|