<P>L'INVENTION A TRAIT AU TRAITEMENT D'ALLIAGES CUIVRE-BERYLLIUM (ET A DES ARTICLES ET PIECES EN CES ALLIAGES AINSI TRAITES) CONTENANT DES QUANTITES FAIBLES PARTICULIERES DE BERYLLIUM ET DE NICKEL, PAR EXEMPLE ENVIRON 0,05 A 0,5 DE BERYLLIUM ET 0,05 A 1 DE NICKEL AVEC POSSIBILITE DE SUBSTITUTION DE COBALT AU NICKEL JUSQU'A CONCURRENCE DE LA MOITIE DE LA TENEUR EN NICKEL AVEC UN RAPPORT DE SUBSTITUTION D'ENVIRON 1 PARTIE EN POIDS DE COBALT POUR 2 PARTIES EN POIDS DE NICKEL, QUI CONFERE A CES ALLIAGES UNE COMBINAISON SUPERIEURE DE RESISTANCE A LA DETENTE DES CONTRAINTES, D'APTITUDE AU FACONNAGE, DE DUCTILITE, DE CONDUCTIBILITE ET DE RESISTANCE MECANIQUE PAR LE PROCESSUS DE RECUIT DE MISE EN SOLUTION, TRAVAIL A FROID A RAISON D'AU MOINS 50 A 70 OU 90 ENVIRON OU PLUS ET DURCISSEMENT PAR VIEILLISSEMENT.</P>
|