| 摘要 |
<p>ALLOY RESISTANT TO SULFURIC ACID CORROSION An air-meltable, castable, workable, weldable alloy resistant to corrosion in sulfuric acid over a wide range of acid strengths. The alloy consists essentially of between about 26.00 and about 29.13% by weight nickel, between about 23.32 and about 28.28% by weight chromium, between about 0.66 and about 1.88% by weight molybdenum, between about 2.50 and about 3.82% by weight copper, between about 3.59 and about 4.72% by weight manganese, between about 0.15 and about 1.15% by weight niobium, up to about 1% by weight titanium, up to about 1.0% by weight tantalum, up to about 0.010% by weight boron, up to about 0.5% by weight cobalt, up to about 0.60% by weight silicon, up to about 0.08% by weight carbon, up to about 0.6% by weight of a rare earth component selected from the group consisting of cerium, lanthanum and misch metal, up to about 0.15% by weight nitrogen, and between about 33.13 and about 39.49% by weight iron.</p> |