发明名称 |
COMPOSITE ARTICLES COMPRISING SPINODAL COPPER-NICKEL-TIN-MANGANESE-PHOSPHORUS ALLOY MATRIX MATERIAL |
摘要 |
A spinodal copper-nickel-tin-manganese alloy is disclosed that contains from 0.001 to about 2 weight percent phosphorus. When combined with small hard particles, the alloy has sufficient fluidity to infiltrate and fill at least 90% of the interstices of the hard particles, resulting in a composite article having superior strength and toughness. This composite article can be used in drilling bits and other cutting tools, either as a support body for cutting elements or as the cutting element itself. |
申请公布号 |
US2016053349(A1) |
申请公布日期 |
2016.02.25 |
申请号 |
US201514832838 |
申请日期 |
2015.08.21 |
申请人 |
Materion Corporation |
发明人 |
Nielsen, JR. William D. |
分类号 |
C22C9/06;C22F1/08;C22C9/02 |
主分类号 |
C22C9/06 |
代理机构 |
|
代理人 |
|
主权项 |
1. A composite article comprising:
a matrix phase comprising a spinodal alloy; and hard particles dispersed within the matrix phase; wherein the spinodal alloy is a Cu—Ni—Sn—Mn—P alloy comprising:
from about 5 wt % to about 22 wt % nickel;from about 4 wt % to about 10 wt % tin;from about 0.05 wt % to about 0.5 wt % manganese;from 0.001 to about 2 wt % phosphorus; andbalance copper. |