| 摘要 |
There is provided a method for producing a Ni-based heat-resistant superalloy, the method comprising the steps of: providing a material to be hot-worked having a composition consisting of, by mass, 0.001 to 0.05% C, 1.0 to 4.0% Al, 4.5 to 7.0% Ti, 12 to 18% Cr, 14 to 27% Co, 1.5 to 4.5% Mo, 0.5 to 2.5% W, 0.001 to 0.05% B, 0.001 to 0.1% Zr, and the balance of Ni with inevitable impurities; heating the material to be hot-worked in a temperature having a range of 1,130 to 1,200°C for at least 2 hours; cooling the material to be hot-worked heated by the heating step to a hot working temperature or less at a cooling rate of at most 0.03°C/second; and subjecting the material to be hot-worked to hot working after the cooling step. A Ni-based heat-resistant superalloy produced by the method has a primary ³' phase with an average particle size of at least 500 nm. |