制造强化玻璃产品方法;Method Of Manufacturing Strengthened Glass Product

摘要

本发明揭露了一种制造强化玻璃产品的方法，其包括：当在100至800 bar的一喷射压力与具有120至600筛孔的尺寸的颗粒下喷射水（H2 O）到该素强化玻璃时，以1至1,500 mm/min的一切割速度切割一素强化玻璃，以制备该强化玻璃；以及藉由具有该强化玻璃之一退火点或更高但低于蒸发点之一温度的一热源以0.001至2.5 mm 2 面积接触至该切割平面，去角化该强化玻璃之一切割平面，以及然后以5至300 mm/sec的速度移动该热源，因而，具有一高生产率且不具有缺陷之该素强化玻璃可快速地被切割，以及该切割平面在一特定条件下被去角化，如此在该切割平面上所产生之微细裂痕可被去除且一高强度可被提供。; and chamfering a cutting plane of the strengthened glass by contacting a heat source having a temperature of an annealing point or more but less than an evaporation point of the strengthened glass to the cutting plane in an area of 0.001 to 2.5 mm 2 , and then moving the heat source at a speed of 5 to 300 mm/sec, thereby, the mother strengthened glass may be quickly cut with a high productivity without defects, and the cutting plane is chamfered under a specific condition, such that fine cracks generated on the cutting plane may be removed and a high strength may be provided.