| 摘要 |
Provided is one aspect of copper alloy sheet containing 4.5% by mass to 12.0% by mass of Zn, 0.40% by mass to 0.90% by mass of Sn, 0.01% by mass to 0.08% by mass of P, as well as 0.005% by mass to 0.08% by mass of Co and/or 0.03% by mass to 0.85% by mass of Ni, the remainder being Cu and unavoidable impurities. The copper alloy sheet satisfies a relationship of 11≦[Zn]+7×[Sn]+15×[P]+12×[Co]+4.5×[Ni]≦17. The one aspect of copper alloy sheet is produced by a production process including a finish cold rolling process at which a copper alloy material is cold-rolled. An average grain size of the copper alloy material is 2.0 μm to 8.0 μm, circular or elliptical precipitates are present in the copper alloy material, and an average particle size of the precipitates is 4.0 nm to 25.0 nm, or a percentage of precipitates having a particle size of 4.0 nm to 25.0 nm makes up 70% or more of the precipitates. |
| 主权项 |
1. A copper alloy sheet that is produced by a production process including a finish cold rolling process at which a copper alloy material is cold-rolled,
wherein an average grain size of the copper alloy material is 2.0 μm to 8.0 μm, circular or elliptical precipitates are present in the copper alloy material, and an average particle size of the precipitates is 4.0 nm to 25.0 nm, or a percentage of the number of precipitates having a particle size of 4.0 nm to 25.0 nm makes up 70% or more of the precipitates, the copper alloy sheet contains 4.5% by mass to 12.0% by mass of Zn, 0.40% by mass to 0.90% by mass of Sn, and 0.01% by mass to 0.08% by mass of P, as well as 0.005% by mass to 0.08% by mass of Co and/or 0.03% by mass to 0.85% by mass of Ni, the remainder being Cu and unavoidable impurities, and [Zn], [Sn], [P], [Co], and [Ni] satisfy a relationship of 11≦[Zn]+7×[Sn]+15×[P]+12×[Co]+4.5×[Ni]≦17 (here, [Zn], [Sn], [P], [Co], and [Ni] represent the contents (% by mass) of Zn, Sn, P, Co, and Ni, respectively). |