Process for preparing catalyst comprising palladium supported on carrier with high dispersion

摘要

A process for preparing a catalyst comprising palladium supported on a carrier via a layered precursor, comprising the following steps: (1) synthesis of hydrotalcite layered precursor which comprises promoting metal element and aluminium on the surface of the carrier of A12O3 microspheres, the atoms of the promoting metal and aluminium being highly dispersed by each other and bonded firmly to the carrier due to the crystal lattice positioning effect of the hydrotalcite crystal; (2) introduction of palladium into the carrier through impregnation; (3) drying; and (4) calcination and reduction with H2, the hydrotalcite layered precursor being converted into a composite oxide which consists of oxides of the promoting metal and aluminium, and the promoting metal element and aluminium being highly dispersed by each other and being able to separate and disperse the mainly active palladium element loaded later. The process has the advantages of improving the catalytic performance of the catalyst, enhancing the stability of the catalyst, and achieving the object of reducing the consumption of the precious metal-palladium.

主权项

1. A process for preparing a supported catalyst containing palladium on a carrier, the process comprising:
(1) preparing M2+Al-LDHs/Al2O3 precursors, including: dissolving an amount of urea into deionized water to obtain a urea solution having a concentration of the urea in the range of 0.2 to 2 mol/L; adding Al2O3 carriers having a mesh size of 26 to 100 with a regular geometry into the urea solution to obtain a second solution, where the content of the Al2O3 carriers is 1 to 6 g/100 mL; stirring the second solution at 80 to 150° C. for 3 to 15 hours to obtain a mixed solution; preparing an M2+ solution by adding an amount of a soluble M2+ salt into deionized water; adding the M2+ solution into the mixed solution, where the concentration of the M2+ solution is in the range of 0.1 to 1 mol/L, stirring under 80 to 160° C. for 3 to 15 hours, cooling, filtering, washing with deionized water, and drying at 80 to 120° C. to thus obtain the M2+Al-LDHs/Al2O3 precursors; and (2) preparing the supported catalyst, including: forming a palladium chloride (PdCl2) aqueous solution, wherein the concentration of the PdCl2 aqueous solution is at 0.03 to 0.3 mol/L; adding the M2+Al-LDHs/Al2O3 precursors prepared in step (1) into the PdCl2 aqueous solution to obtain a solution, and placing the obtained solution into a shaker under 50 to 90° C. water bath for 1 to 24 hours; filtering the obtained solution, washing with deionized water, drying at 80 to 120° C., and calcining at 300 to 900° C. for 2 to 24 hours to obtain a calcined product; and treating the calcined product by a reduction process under H2 atmosphere at 200 to 600° C. for 2 to 24 hours to obtain the supported catalyst, wherein the shape of the Al2O3 carriers is one or more types of a spherical shape, a clover shape, and a sheet-like shape, and the crystalline form of the Al2O3 carriers is one or more types of δ,β,γ,θ and η, and wherein M2+ of the M2+Al-LDHs/Al2O3 precursors is one or more types of Mg2+, Ni2+, Ca2+ and Cu2+.