| 摘要 |
Provided are an epitaxial silicon carbide single crystal substrate having a high-quality silicon carbide single crystal thin film with less stacking faults on a silicon carbide single crystal substrate and a production method therefor. The epitaxial silicon carbide single crystal substrate is produced by growing a silicon carbide epitaxial layer on a silicon carbide single crystal substrate having an off-angle of 4° or less so that the number of stacking faults emitting light at wavelengths ranging from 400 to 600 nm by photoluminescence on the substrate is less than 10/cm2 in total. Additionally, the method for producing the epitaxial silicon carbide single crystal substrate forms the epitaxial layer by using chlorosilane as a silicon-based material gas and hydrocarbon gas as a carbon-based gas, at a growth temperature of 1600° C. to 1700° C., at a C/Si ratio of 0.5 to 1.0, and at a growth rate of 1 to 3 mum/hr. |