BIMODAL POLYETHYLENE RESINS THAT HAVE HIGH STIFFNESS AND HIGH ESCR

摘要

A bimodal polyethylene having a high density ranging from about 0.955 to about 0.959 g/cc, an improved environmental stress cracking resistance (ESCR) of from about 400 to about 2500 hours, and an improved 0.4% flesxural modulus of from about 180,000 to about 260,000 psi (1,200 MPa to about 1,800 MPa) may be formed using a Ziegler-Natta polymerization catalyst using two reactors in series. The bimodal polyethylene may have a high load melt index (HLMI) of from about 2 and about 30 dg/min and may be optionally made with a small amount of alpha-olefinic comonomer in the second reactor. It is emphasized that this abstract is provided to comply with the rules requiring an abstract which will allow a searcher or other reader to quickly ascertain the subject matter of the technical disclosure. It is submitted with the understanding that it will not be used to interpret or limit the scope or meaning of the claims. 37 CFR 1.72(b).