<p>There is claimed a sheet or plate structural member suitable for aerospace applications and having improved combinations of strength and toughness. The member is made from a substantially vanadium-free aluminum-based alloy consisting essentially of: about 4.85-5.3 wt.% copper, about 0.5-1.0 wt.% magnesium, about 0.4-0.8 wt.% manganese, about 0.2-0.8 wt.% silver, about 0.05-0.25 wt.% zirconium, up to about 0.1 wt.% silicon, and up to about 0.1 wt.% iron, the balance aluminum, incidental elements and impurities, the Cu:Mg ratio of said alloy being between about 5 and 9, and more preferably between about 6.0 and 7.5. The invention exhibits a typical tensile yield strength of about 77 ksi or higher at room temperature and can be processed into various lower wing members or into the fuselage skin of high speed aircraft.</p> |