Herstellung von gemischten Pulvern

摘要

A method of preparing a mixture of zirconia and a stabilising agent for the zirconia comprises milling an aqueous suspension of particulate zirconia and particulate stabilising agent in a bead mill for at least 2 minutes in the presence of a particulate mixing medium having an average particle size from 0.2 mm to 3 mm. Preferred stabilising agents are oxides of yttrium, cerium, calcium or magnesium. Surprisingly, ceramics prepared from the product mixture are more resistant to degradation by attack from water above 100 DEG C than are ceramics prepared from coprecipitated powders.