Low molecular weight polymers of acrylic esters

摘要

Low molecular weight polymers of acrylic esters which are suitable for use as external plasticizers in coated compositions on a synthetic resin basis are obtainable by subjecting (a) from 80 to 100% by weight of at least one acrylic ester of C1-C8-alkanol (monomer I) and (b) 0 to 20% by weight of one or more other copolymerizable monomers (monomer II) to a free radical polymerization in a solution in isopropanol in a pressure vessel at 130 DEG -140 DEG C. by introducing first from 70 to 95% by weight of a solvent and adding the remainder of the polymerization batch continuously over 3-7 hours in separate portions of which one contains the monomers and, after the polymerization has ended, distilling off the solvent under reduced pressure, the weight proportion of solvent being 5-15% by weight based on the monomers, the weight proportion of initiator being 0.5-3% by weight based on the monomers, and the half-life of the initiator at the polymerization temperature being from 10 seconds to 3 hours.