Urethane-modified polyester resin which has a total acid value not greater than 10 KOH mg/g and is obtained by kneading, in a molten state, a base polyester resin (A) having an acid value of 5 to 20 KOH mg/g and a hydroxyl value of 40 to 70 KOH mg/g, a low-molecular-weight polyester resin (B) having an acid value not greater than 5 KOH mg/g, a hydroxyl value not greater than 10 KOH mg/g and a weight-average molecular weight of 3,000 to 5,000 and a polyisocyanate compound, wherein components (A) and (B) are at a weight ratio of 3 to 5:7 to 5 and the polyisocyanate compound is in an amount of 0.2 to 1.2 equivalent, in terms of an isocyanate group per equivalent, of the total hydroxyl groups of all the resins.
|