| 摘要 |
PURPOSE:To provide the titled resin compsn. having excellent moldability, mechanical strength, flexibility and heat resistance, consisting of a polyolefin, a higher fatty acid monoglyceride, calcium salt of a higher aliph. monocarboxylic acid and zinc salt of a higher aliph. monocarboxylic acid. CONSTITUTION:0.05-1wt% higher fatty acid monoglyceride (A) having a purity of 90% or above, 0-0.3wt% calcium salt of a 10C or higher aliph. monocarboxylic acid (B) (e.g. calcium laurate) and 0-0.3wt% zinc salt of a 10C or higher aliph. monocarboxylic acid (C) (e.g. zinc laurate) are added to a polyolefin having an MFR10 of 0.05-10g/10min under a 10kg load, a Q value of 2-10 and a density of 0.900-0.930g/cm<3> (e.g. high-pressure PE) in such a proportion that the combined amount of components B and C is 0.5wt% or below. The mixture is melt-kneaded at 120-250 deg.C. |