| 摘要 |
The retention of the beta brass phase structure (body-centered cubic) as gold atoms (molars) are substituted for copper atoms. Thus essentially the useful physical and working properties of the beta brasses are retained (hot forgeability, castability, some ductility etc.). As to chemical behavior, there is a definite nobleization effect of the beta brasses, i.e. all gold-containing beta golds are more tarnish resistant than the beta brasses, and the nobleization increases with gold content. However, of most importance from a commercial point of view, is that the low kt beta golds (4-kt, 6-kt) are more tarnish resistant than the 10-kt conventional jewelry alloys, and equal to those of 14-kt gold. In essence there is a tarnish resistance enhancement in going from alpha structure to beta structure kt for kt, in the jewelry range. Other noble metals (Pd, Pt, Ru, Rh, Os, Ir and Ag) may be used singly or in combinations with, or in lieu of, the gold.
|