Process for making low and specified hardenability structural steel

摘要

A process for making desired low (LH) hardenability steels in an electric arc or, induction furnace, which is loaded with metal charge consisting of iron, carbon, alloy, scrap with a specified maximum content of manganese, silicon, chrome, nickel and copper, providing for the final content of each of them of not more than 0.1 weight % followed by carburization in a ladle or ladle furnace, the melt then deoxidized in the ladle or ladle furnace with aluminum (1.0-2.3 kg/t), titanium or vanadium in order to achieve the desired low hardenability DI. The invention makes it possible to obtain better mechanical properties and stable hardenability characterized by the particular desired DI.

主权项

1. A process for smelting low hardenability (LH) structural steel comprising, loading a charge in one of an electric arc, an induction furnace or a converter with iron carbon alloy, with a specified maximum content of manganese, silicon, chrome, nickel and copper, content of each of them of not more than 0.1 weight %, heating of the charge to a temperature corresponding to a beginning of refining, followed by carburization in a ladle or ladle furnace, a refining and a pure rimming period done by flushing a portion of slag from the furnace or converter and a recurrent addition of slag-forming materials to the remaining portion of the slag to keep a content of each of the manganese, silicon, chrome, nickel and copper in a melt during tapping to not more than 0.1 weight % deoxidizing the melt in the ladle or ladle furnace with aluminum, titanium and vanadium, with 0.3-0.5 weight % of a total amount of aluminum, titanium and vanadium added to the ladle or ladle furnace and a remaining amount until not less than 30% of the ladle or ladle furnace volume is filled, whereas titanium, vanadium and nitrogen are added after aluminum, making sure the metal in the ladle or ladle furnace contains 0.3-1.2 weight % carbon, 0.03-0.10 weight % aluminum, 0-0.4 weight % titanium, 0-0.4 weight % vanadium, 0 to 0.15 weight % nitrogen so as to achieve a steel of a particular Ideal Diameter (DI) value in the range of 6-15 mm after Through Surface Hardening (TSH) hardening.