| 摘要 |
Lithium rich metal oxyfluorides are described with high specific capacity and, good cycling properties. The materials have particularly good high rate capabilities. The fluorine dopant can be introduced in a low temperature process to yield the materials with desirable cycling properties. In some embodiments, the positive electrode active materials have a composition represented approximately by the formula Li1+xNiαMn&bgr;CoγAδO2−zFz where: x is from about 0.02 to about 0.19, α is from about 0.1 to about 0.4, &bgr; is from about 0.35 to about 0.869, γ is from about 0.01 to about 0.2, δ is from 0.0 to about 0.1 and z is from about 0.01 to about 0.2, where A is Mg, Zn, Al, Ga, B, Zr, Ti, Ca, Ce, Y, Nb or combinations thereof. |