| 摘要 |
<P>PROBLEM TO BE SOLVED: To obtain an antireflection hard coat film having continuously and uniformly a satisfactory appearance free from brushing. <P>SOLUTION: In a method of manufacturing a hard coat film, a hard coat layer and an antireflection layer are laminated in order on at least one surface of a resin film at a temperature of 15 to 30°C in an atmosphere of 7.0g/m<SP>3</SP>absolute humidity, and just after coating of respective layers, a coating surface is exposed to air of 1.0m/sec wind velocity to dry the layers, and thus the antireflection hard coat film is manufactured. Preferably, the temperature of air blasted to the coating surface is set within a range of 15 to 150°C, and they are dried within 20 seconds after coating. <P>COPYRIGHT: (C)2006,JPO&NCIPI |