Method for high speed chromium plating of cylindrical articles

摘要

A method for the high speed chromium plating of piston rings, cylinder liners and the like wherein the cathodic workpiece is rotated at a peripheral speed of 1-4 m/sec. relative to a concentrically disposed anode. The latter may comprise a single spoked member or a plurality of rectangular pieces to thereby create a turbulence in the electrolyte bath. When a cylindrical anode is used, a bladed agitator is secured to the rotating workpiece to generate turbulence. The interelectrode spacing is from 0.1 to 4t cm with a multipolar anode, where t is the thickness of an anode pole. The current density is from 200 - 600 amps/dm2, and the bath temperature is from 20 DEG - 50 DEG C or from 65 DEG - 80 DEG C, depending on the plating characteristics desired.