CONTINUOUS PROCESS FOR COATING STEEL WIRE CORD

摘要

Continuous processes for producing a coated steel wire are provided. The processes entail wetting steel wire in an aqueous solution comprising at least 95% water and 0.01 to 5% weight/weight of the carboxylic acid salt of an alkoxy modified silsesquioxane of formula (I), evaporating water from the wet coated steel wire to form a mostly-dry coated steel wire and then heating (one or more steps) the mostly-dry coated steel wire at a temperature of 50-240° C. such that the steel wire reaches a minimum temperature of at least 110° C. in at least one step, thereby forming a dry coated steel wire. The coated steel wire is optionally covered with rubber skim or otherwise embedded into rubber and can be incorporated into various objects including tires, conveyor belts, hoses and the like. The silsesquioxane coating improves adhesion between the steel wire and the rubber skim/other rubber covering.