This invention is concerned with the processing method of carburized product with an increased hardening depth, in which boron treated steel comprising by weight percent 0.18 SIMILAR 0.35 % C, 0.06 SIMILAR 0.3 % Si, 0.5 SIMILAR 1.5 % Mn, <1 % Cr, <0.02 % S, <0.03 % P, 0.01 SIMILAR 0.08 % Al, <0.05 % Ti, <0.012 % N2, <0.003 % O2 and 0.0005 SIMILAR 0.003 % B is carburized at the temperature range of 925 SIMILAR 1050 DEG C. As described in the above, if the steel products made of boron treated steel are <IMAGE> |