| 摘要 |
A method for providing a uniformly dense polymer foam body having a density between about 0.013 g/cm3 to about 0.5 g/cm3 is disclosed. The method utilizes a thermally expandable polymer microballoon material wherein some of the microballoons are unexpanded and some are only partially expanded. It is shown that by mixing the two types of materials in appropriate ratios to achieve the desired bulk final density, filling a mold with this mixture so as to displace all or essentially all of the internal volume of the mold, heating the mold for a predetermined interval at a temperature above about 130° C., and then cooling the mold to a temperature below 80° C. the molded part achieves a bulk density which varies by less then about ±6% everywhere throughout the part volume.
|